WEICON F Epoxy Resin 0.5 kg

Composition

Epoxy resin aluminium-filled

Specific Properties

Pasty

Colour after curing

aluminium

Density of the mixture (200g preparation)

1,6 g/cm3

Consumption at a coating thickness of 1,0 mm

1,60 kg/m2

Maximium layer thickness for each working step

10 mm

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

60 Mpa

Pull

20 Mpa

Bending

37 Mpa

E-Modul

1.500 to 2.000 Mpa

Shore D (ATSM D 1706)

84

Shrinkage

0,025 %

Thermoforming resistance

+55 deg C

Thermoforming resistance

+60 deg C

Temperature resistance

-35 to +120 deg C

Thermal diffusivity (23 deg C)

0,908 mm2/s

ISSA-Code

75.509.09/10

IMPA-Code

812921/22