WEICON Ceramic W Epoxy Resin 0.5 kg

Composition

Epoxy resin mineral-filled

Specific Properties

Putty , extremely wear resistant

Colour after curing

White

Density of the mixture (200g preparation)

1,59 g/cm3

Consumption at a coating thickness of 1,0 mm

1,59 kg/m2

Maximum layer thickness for each working step

10 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

120 min.

Curing time mechanical loads

24 h

Final hardness after

48 h

Pull

30 Mpa

Bending

90 Mpa

Shore D (ATSM D 1706)

85

Shrinkage

0,02 %

Tg after curing at room temperature

60,3 Tg (deg C)

Tg after tempering (at 120 deg C)

144 Tg (deg C)

Thermoforming resistance

+150 deg C

Temperature resistance

-35 to +200 briefly to +260 deg C