Flex 310 M HT 200 MS-Polymer Adhesive 310 ml Grey

Composition

1 C.-MS Polymer

Density  

1,41 g/cm³

Viscosity adhesive

pasty

Stability/Run-off (ASTM D 222)

< 1 mm

Processing temperature

 +5 to +35 °C

Cure type

By humidity

Curing condition

+5 to +40°C and 30% to 95% rel. humidity

Skin-overtime*

10 min.

Cure speed (first 24h)

3 -4 mm

Shelf life (+5°C to +25°C / +41°F to +77°F)

12 months

Shore A hardness (DIN 5355 / ASTM D 224)

± 5 55

Elongation at break (DIN 53504/ASTM D 2240)

± 5 400 %

Tensile strength of pure adhesive and sealant

3,2 N/mm²

Tear strength (DIN 53515/ASTM D 1002)

21 N/mm²

Overpaintable (liquid paint)

only after total cure

Building material category (DIN 412)

 B 2

Specific forward resistance

3,4 x 10^11 Ohm/cm

Layer thickness

2,0 mm

Temperature resistance

-40 to +90 (45 min. +180 / 30 min. +200) °C

ISSA-Code

75.634.37

IMPA-Code

81 52 77/78